STAINLESS STEEL FLUX-CORED WIRE
Brand Size(mm) Equivalent Specification Welding Position Type Of Current/Gas Typical Chemical Composition Of Deposited Metal(wt%) Typical Mechanical Properties Of Deposited Metal Application
C Cr Ni Mo Mn Si P S Cu Others Y.P.(Mpa) T.S.(Mpa) E.L.(%) I.V.(J)
WFS-308 1.2/1.6 GB/T TS308-FC11
AWS E308T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.029 19.82 9.61 0.01 1.24 0.63 0.018 0.008 0.01 - - 610 41 - Used for welding stainless steel structural parts of the same type (06Cr19Ni10). 
WFS-308L 1.2/1.6 GB/T TS308L-FC11
AWS E308LT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.022 19.51 9.47 0.01 1.52 0.77 0.019 0.003 0.01 - - 590 43 - For welding 022Cr19Ni10 stainless steel and for corrosion resistant 06Cr18Ni11Ti stainless steel structural parts whose working temperature is lower than 300℃.
WFS-308H 1.2/1.6 GB/T TS308H-FC11
AWS E308HT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.049 19.50 9.69 0.02 1.40 0.71 0.026 0.003 0.02 - - 605 41 - Widely used in petrochemical and chemical plants, especially in the manufacture of rotary separators, catalytic cracking unit for the production of catalyst recycling pipelines.
WFS-309L 1.2/1.6 GB/T TS309L-FC11
AWS E309LT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.036 24.31 12.10 0.02 1.48 0.73 0.023 0.002 0.06 - - 590 40 - For welding the same type of stainless steel structure, composite steel and dissimilar steel components, which are manufactured by petrochemical equipment with working temperature below 400℃, can also be used for caldding of transition layer.
WFS-309LD 1.2/1.6 GB/T TS309L-FC10
AWS E309LT0-1
PA,PB DC+/CO2 0.026 24.20 12.77 0.02 1.25 0.61 0.025 0.003 0.06 - - 580 39 - For cladding of inner wall of hydrogenation reactor or pressure vessel and transition layer of clad plate. 
WFS-309LMo 1.2/1.6 GB/T TS309LMo-FC11
AWS E309LMoT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.035 24.18 12.58 2.57 1.57 0.57 0.014 0.003 0.01 - - 585 37 - For welding ultra-low carbon stainless steel structure (such as urea converter lining), composite steel and dissimilar steel components with working temperature below 300℃.It can also be used for transition layer caldding.
WFS-316L 1.2/1.6 GB/T TS316L-FC11
AWS E316LT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.034 19.15 12.27 2.64 1.64 0.60 0.017 0.005 0.03 - - 580 38 - It can be used to weld the same type of ultra-low carbon stainless steel structure (such as urea synthesis tower lining), and also can be used to weld dissimilar steel.
WFS-317L 1.2/1.6 GB/T TS317L-FC11
AWS E317LT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.025 18.30 13.7 3.3 1.73 0.41 0.018 0.005 0.02 - - 560 34 - On the basis of 316L, the pitting corrosion resistance is better by adding 1%Mo. 
WFS-310 1.2 GB/T TS310-FC11
AWS E310T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.12 25.78 20.25 0.01 2.41 0.59 0.011 0.003 0.01 - - 595 38 - For high temperature resistant products, such as high temperature furnace, coal coking equipment, can also be used for clad surfacing and dissimilar steel welding.
WFS-310(Basic) 1.2 GB/T TS310-FC11
AWS E310T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.12 25.28 20.18 0.06 2.41 0.20 0.013 0.005 0.02 - - 590 40 - On the basis of 310, the crack resistance was improved by alkaline formulation. 
WFS-347L 1.2/1.6 GB/T TS347-FC11
AWS E347T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.022 19.66 9.38 0.02 1.45 0.64 0.019 0.002 0.01 Nb+Ta:0.38 - 590 39 - For welding 06Cr18Ni11 corrosion-resistant stainless steel with titanium or niobium stability. 
WFS-347LD 1.2/1.6 GB/T TS347-FC10
AWS E347T0-1
PA,PB DC+/CO2 0.021 19.95 9.81 0.01 1.44 0.46 0.017 0.001 0.01 Nb+Ta:0.34 - 580 40 - Cladding corrosion resistant layer on inner wall of hot-wall hydrogenation reactor.
WFS-312 1.2 GB/T TS312-FC11
AWS E312T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.050 28.5 8.5 0.01 1.2 0.6 0.016 0.002 0.01 - - 740 24 - It can be used for welding high nickel alloy and other metals, because of its excellent crack resistance. It can also be used for welding high carbon steel, tool steel, dissimilar steel and surfacing of transition layer.
WFS-2209 1.2 GB/T TS2209-FC1
AWS E2209T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.024 23.11 9.20 3.18 1.25 0.65 0.015 0.003 0.02 N:0.16 - 750 28 - Austenite-ferrite duplex stainless steel is suitable for welding of SUS S2205 S31803 in petrochemical industry. 
WFS-2594 1.2 GB/T TS2594-FC10
AWS E2594T0-1
PA,PB DC+/CO2 0.023 25.55 9.61 3.67 0.73 0.61 0.021 0.008 0.02 N:0.26 - 830 23 - Austenite-ferrite super duplex stainless steel with excellent pitting corrosion resistance is suitable for welding of UNS S32750 and other steels.
WFS-198 1.2 - PA,PB,PC,PD,PE,PF DC+/CO2 0.041 19.86 9.22 0.02 1.19 0.54 0.020 0.004 0.02 - - 590 32 - It has high ferrite content, excellent thermal resistance and intergranular corrosion resistance. It is suitable for 304 stainless steel working below 300℃.
WFS-385 1.2 - PA,PB,PC,PD,PE,PF DC+/80%Ar+20%CO2 0.026 20.38 24.51 4.22 1.60 0.45 0.016 0.002 1.45 - - 595 40 - Super austenitic stainless steel with excellent corrosion resistance. 
WFS-410NiMo 1.2/1.6 GB/T TS410NiMo-FC11
AWS E410NiMoT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.044 11.85 4.43 0.56 0.48 0.52 0.019 0.005 0.01 - - 842 19 - It is suitable for wear-resistant and corrosion-resistant occasions such as turbine rotor valves with stricter requirements. 
WFS-253MA 1.2 - PA,PB,PC,PD,PE,PF DC+/CO2 0.051 21.49 10.35 0.15 0.79 1.80 0.016 0.004 - N:0.13
Re:0.025
- 665 46 - Ferro-based 22%Cr-10%Ni alloy with rare earth element content of C, Si, N and Ce controlled has excellent oxidation resistance. It is suitable for industrial furnaces and furnaces, high temperature flue, exhaust gas emission devices, etc.
WCS-409Ti 1.0/1.2 GB/T TS409-MM131
AWS EC409
PA,PB,PC,PD,PE,PF DC+/Ar 0.047 11.04 0.01 0.01 0.54 0.36 0.011 0.008 0.01 Ti:0.59 - 490 19 - Metal core flux cored wire is suitable for cold end welding of automobile exhaust system and muffler. 
STAINLESS STEEL FLUX-CORED WIRE
Brand Size(mm) Equivalent Specification Welding Position Type Of Current/Gas Typical Chemical Composition Of Deposited Metal(wt%) Typical Mechanical Properties Of Deposited Metal Application
C Cr Ni Mo Mn Si P S Cu Others Y.P.(Mpa) T.S.(Mpa) E.L.(%) I.V.(J)
WFS-308 1.2/1.6 GB/T TS308-FC11
AWS E308T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.029 19.82 9.61 0.01 1.24 0.63 0.018 0.008 0.01 - - 610 41 - Used for welding stainless steel structural parts of the same type (06Cr19Ni10). 
WFS-308L 1.2/1.6 GB/T TS308L-FC11
AWS E308LT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.022 19.51 9.47 0.01 1.52 0.77 0.019 0.003 0.01 - - 590 43 - For welding 022Cr19Ni10 stainless steel and for corrosion resistant 06Cr18Ni11Ti stainless steel structural parts whose working temperature is lower than 300℃.
WFS-308H 1.2/1.6 GB/T TS308H-FC11
AWS E308HT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.049 19.50 9.69 0.02 1.40 0.71 0.026 0.003 0.02 - - 605 41 - Widely used in petrochemical and chemical plants, especially in the manufacture of rotary separators, catalytic cracking unit for the production of catalyst recycling pipelines.
WFS-309L 1.2/1.6 GB/T TS309L-FC11
AWS E309LT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.036 24.31 12.10 0.02 1.48 0.73 0.023 0.002 0.06 - - 590 40 - For welding the same type of stainless steel structure, composite steel and dissimilar steel components, which are manufactured by petrochemical equipment with working temperature below 400℃, can also be used for caldding of transition layer.
WFS-309LD 1.2/1.6 GB/T TS309L-FC10
AWS E309LT0-1
PA,PB DC+/CO2 0.026 24.20 12.77 0.02 1.25 0.61 0.025 0.003 0.06 - - 580 39 - For cladding of inner wall of hydrogenation reactor or pressure vessel and transition layer of clad plate. 
WFS-309LMo 1.2/1.6 GB/T TS309LMo-FC11
AWS E309LMoT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.035 24.18 12.58 2.57 1.57 0.57 0.014 0.003 0.01 - - 585 37 - For welding ultra-low carbon stainless steel structure (such as urea converter lining), composite steel and dissimilar steel components with working temperature below 300℃.It can also be used for transition layer caldding.
WFS-316L 1.2/1.6 GB/T TS316L-FC11
AWS E316LT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.034 19.15 12.27 2.64 1.64 0.60 0.017 0.005 0.03 - - 580 38 - It can be used to weld the same type of ultra-low carbon stainless steel structure (such as urea synthesis tower lining), and also can be used to weld dissimilar steel.
WFS-317L 1.2/1.6 GB/T TS317L-FC11
AWS E317LT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.025 18.30 13.7 3.3 1.73 0.41 0.018 0.005 0.02 - - 560 34 - On the basis of 316L, the pitting corrosion resistance is better by adding 1%Mo. 
WFS-310 1.2 GB/T TS310-FC11
AWS E310T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.12 25.78 20.25 0.01 2.41 0.59 0.011 0.003 0.01 - - 595 38 - For high temperature resistant products, such as high temperature furnace, coal coking equipment, can also be used for clad surfacing and dissimilar steel welding.
WFS-310(Basic) 1.2 GB/T TS310-FC11
AWS E310T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.12 25.28 20.18 0.06 2.41 0.20 0.013 0.005 0.02 - - 590 40 - On the basis of 310, the crack resistance was improved by alkaline formulation. 
WFS-347L 1.2/1.6 GB/T TS347-FC11
AWS E347T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.022 19.66 9.38 0.02 1.45 0.64 0.019 0.002 0.01 Nb+Ta:0.38 - 590 39 - For welding 06Cr18Ni11 corrosion-resistant stainless steel with titanium or niobium stability. 
WFS-347LD 1.2/1.6 GB/T TS347-FC10
AWS E347T0-1
PA,PB DC+/CO2 0.021 19.95 9.81 0.01 1.44 0.46 0.017 0.001 0.01 Nb+Ta:0.34 - 580 40 - Cladding corrosion resistant layer on inner wall of hot-wall hydrogenation reactor.
WFS-312 1.2 GB/T TS312-FC11
AWS E312T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.050 28.5 8.5 0.01 1.2 0.6 0.016 0.002 0.01 - - 740 24 - It can be used for welding high nickel alloy and other metals, because of its excellent crack resistance. It can also be used for welding high carbon steel, tool steel, dissimilar steel and surfacing of transition layer.
WFS-2209 1.2 GB/T TS2209-FC1
AWS E2209T1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.024 23.11 9.20 3.18 1.25 0.65 0.015 0.003 0.02 N:0.16 - 750 28 - Austenite-ferrite duplex stainless steel is suitable for welding of SUS S2205 S31803 in petrochemical industry. 
WFS-2594 1.2 GB/T TS2594-FC10
AWS E2594T0-1
PA,PB DC+/CO2 0.023 25.55 9.61 3.67 0.73 0.61 0.021 0.008 0.02 N:0.26 - 830 23 - Austenite-ferrite super duplex stainless steel with excellent pitting corrosion resistance is suitable for welding of UNS S32750 and other steels.
WFS-198 1.2 - PA,PB,PC,PD,PE,PF DC+/CO2 0.041 19.86 9.22 0.02 1.19 0.54 0.020 0.004 0.02 - - 590 32 - It has high ferrite content, excellent thermal resistance and intergranular corrosion resistance. It is suitable for 304 stainless steel working below 300℃.
WFS-385 1.2 - PA,PB,PC,PD,PE,PF DC+/80%Ar+20%CO2 0.026 20.38 24.51 4.22 1.60 0.45 0.016 0.002 1.45 - - 595 40 - Super austenitic stainless steel with excellent corrosion resistance. 
WFS-410NiMo 1.2/1.6 GB/T TS410NiMo-FC11
AWS E410NiMoT1-1
PA,PB,PC,PD,PE,PF DC+/CO2 0.044 11.85 4.43 0.56 0.48 0.52 0.019 0.005 0.01 - - 842 19 - It is suitable for wear-resistant and corrosion-resistant occasions such as turbine rotor valves with stricter requirements. 
WFS-253MA 1.2 - PA,PB,PC,PD,PE,PF DC+/CO2 0.051 21.49 10.35 0.15 0.79 1.80 0.016 0.004 - N:0.13
Re:0.025
- 665 46 - Ferro-based 22%Cr-10%Ni alloy with rare earth element content of C, Si, N and Ce controlled has excellent oxidation resistance. It is suitable for industrial furnaces and furnaces, high temperature flue, exhaust gas emission devices, etc.
WCS-409Ti 1.0/1.2 GB/T TS409-MM131
AWS EC409
PA,PB,PC,PD,PE,PF DC+/Ar 0.047 11.04 0.01 0.01 0.54 0.36 0.011 0.008 0.01 Ti:0.59 - 490 19 - Metal core flux cored wire is suitable for cold end welding of automobile exhaust system and muffler. 
Tel
+86-21-69933003
Feedback
WeChat

Professional production of "O" brand welding materials

Service Hotline +86-21-699330030 Monday to Friday
AM: 09:00~12:00 PM: 13:00~18:00

Contact

Add: No.426, Ju Mun Village, Wai gang Town, Jiading District, Shanghai
Tel: +86-21-69933003
Fax: +81-21-69931040
E-mail: info@musicfantalk.com
Website: musicfantalk.com

Scan it