BACK SELF-SHIELDED STAINLESS STEEL COATED WIRE
Brand Size(mm) Equivalent Specification Welding Position Type Of Current Typical Chemical Composition Of Deposited Metal(wt%) Typical Mechanical Properties Of Deposited Metal Application
C Mn Si P S Cr Ni Mo Cu Others Y.P.(Mpa) T.S.(Mpa) E.L.(%) I.V.(J)
TGF308 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.029 1.1 0.6 0.024 0.007 19.98 9.89 0.02 0.01 - - 605 41 - Argon free back self-shielded one-sided welding with two-sided formed coating wire is used for SUS304 stainless steel welding.
TGF308L 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.021 1.15 0.63 0.023 0.007 19.85 9.88 0.02 0.02 - - 605 41 - Argon free back self-shielded one-sided welding with two-sided formed coating wire is used for SUS304L stainless steel welding.
TGF309L 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.021 1.25 0.53 0.022 0.007 24.55 13.51 0.02 0.01 - - 600 39 - Argon-free back self-shielded one-sided and double-sided formed coated wire is used for welding stainless steel and carbon steel or low alloy steel dissimilar steel.
TGF316L 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.023 1.18 0.46 0.018 0.002 19.42 11.38 2.37 0.02 - - 555 39 - Argon free back self-shielded one-sided welding with two-sided formed coating wire is used for welding stainless steel SUS316 and SUS316L. 
TGF347 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.026 1.42 0.77 0.024 0.003 19.82 9.33 0.10 0.06 Nb:0.4 - 590 40 - Argon free back self-shielded one-sided welding with double-sided forming flux-coated wire is used for welding stainless steel SUS321 and SUS347.
TGF2209 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.019 0.97 0.75 0.023 0.002 22.91 8.90 3.30 0.01 N:0.18 - 710 25 - Argon free back self-shielded one-sided and double-sided formed coated wire is used for SUS2205 and other 22% Cr duplex stainless steel welding.
BACK SELF-SHIELDED STAINLESS STEEL COATED WIRE
Brand Size(mm) Equivalent Specification Welding Position Type Of Current Typical Chemical Composition Of Deposited Metal(wt%) Typical Mechanical Properties Of Deposited Metal Application
C Mn Si P S Cr Ni Mo Cu Others Y.P.(Mpa) T.S.(Mpa) E.L.(%) I.V.(J)
TGF308 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.029 1.1 0.6 0.024 0.007 19.98 9.89 0.02 0.01 - - 605 41 - Argon free back self-shielded one-sided welding with two-sided formed coating wire is used for SUS304 stainless steel welding.
TGF308L 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.021 1.15 0.63 0.023 0.007 19.85 9.88 0.02 0.02 - - 605 41 - Argon free back self-shielded one-sided welding with two-sided formed coating wire is used for SUS304L stainless steel welding.
TGF309L 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.021 1.25 0.53 0.022 0.007 24.55 13.51 0.02 0.01 - - 600 39 - Argon-free back self-shielded one-sided and double-sided formed coated wire is used for welding stainless steel and carbon steel or low alloy steel dissimilar steel.
TGF316L 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.023 1.18 0.46 0.018 0.002 19.42 11.38 2.37 0.02 - - 555 39 - Argon free back self-shielded one-sided welding with two-sided formed coating wire is used for welding stainless steel SUS316 and SUS316L. 
TGF347 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.026 1.42 0.77 0.024 0.003 19.82 9.33 0.10 0.06 Nb:0.4 - 590 40 - Argon free back self-shielded one-sided welding with double-sided forming flux-coated wire is used for welding stainless steel SUS321 and SUS347.
TGF2209 2.0/2.5 - PA,PB,PC,PD,PE,PF DC- 0.019 0.97 0.75 0.023 0.002 22.91 8.90 3.30 0.01 N:0.18 - 710 25 - Argon free back self-shielded one-sided and double-sided formed coated wire is used for SUS2205 and other 22% Cr duplex stainless steel welding.
Tel
+86-21-69933003
Feedback
WeChat

Professional production of "O" brand welding materials

Service Hotline +86-21-699330030 Monday to Friday
AM: 09:00~12:00 PM: 13:00~18:00

Contact

Add: No.426, Ju Mun Village, Wai gang Town, Jiading District, Shanghai
Tel: +86-21-69933003
Fax: +81-21-69931040
E-mail: info@musicfantalk.com
Website: musicfantalk.com

Scan it